Labor

Non-Precious Metal Alloys

CAM-Materials

Work Preparation and Model Production

Modelation

Embedding and Investment

Surface Processing

Ceramic Materials

Prosthetics

Dentist

Work Preparation and Model Production

Prosthetics

Miscellaneous supplies for the dental practice

Medical

Work Preparation and Model Production

Miscellaneous supplies for the dental practice

Labor_logo
TELESKOPARBEITEN 01
TELESKOPARBEITEN 02
TELESKOPARBEITEN 03
Starbond CoS
Starbond CoS
REF - Table
CoCr-premium bonding alloy – free of nickel and beryllium – ...

█ SPECIFICATION

CoCr-premium bonding alloy – free of nickel and beryllium –
  • Extremely corrosion resistant.
  • Bio-compatible.
  • Especially patient-friendly due to a low thermal conductivity.
  • Ease of processing and polishing due to a low hardness of 280 HV.
  • A thermal expansion coeffi cient of 14,0 ensures fl exibility when choosing the ceramics.
  • Depending on the ceramics, no cooling period is required.
  • A light oxide makes for perfect esthetics.
  • High bonding strength with ceramic masses.
  • Suitable for laser welding.
Composition:
Co Cr W Mo Si
Other ingredients <1%
59 % 25 % 9,5 % 3,5 % 1 %
 C, Fe, Mn, N
Technical properties:    


  Other properties:
Proof stress 650 MPa  

Ultimate tensile strength 910 MPa   Density 8,8 g/cm³
Tensile elongation 8 %   Solidus-Liquidus interval 1305 - 1400°C
Elastic modulus 200 GPa   Casting temperature 1500 - 1550°C
Vickers hardness 280-HV 10   Thermal expansion coeffi cient 14 μm/m °C
  REF
1000 g 133000
250 g 133250

MoguCera C
MoguCera C
REF - Table
CoCr- bonding alloy – free of nickel and beryllium – ...

█ SPECIFICATION

CoCr- bonding alloy – free of nickel and beryllium –
  • Extremely corrosion resistant.
  • Bio-compatible.
  • Especially patient-friendly due to a low thermal conductivity.
  • Ease of processing and polishing due to a low hardness of 300 HV 10.
  • A thermal expansion coeffi cient of 14,1 ensures fl exibility when choosing the ceramics.
  • High bonding strength with ceramic masses.
  • Suitable for laser welding.
Composition:
Co Cr Mo Mn Other ingredients <1%
65 % 28 % 5 % 1 % C, Si
Technical properties:    


  Other properties:
Proof stress 508 MPa  

Ultimate tensile strength 795 MPa   Density 8.3 g/cm³
Tensile elongation 9 %   Solidus-Liquidus interval 1370-1435 °C
Elastic modulus 209 GPa   Casting temperature 1535-1590 °C
Vickers hardness 300 HV 10   Thermal expansion coeffi cient 14.1 μm/m °C
  REF
1000 g 138000

Starbond LFC
Starbond LFC
REF - Table
LFC-Bonding alloy with a wide spectrum of indications – free of nickel and beryllium –

█ SPECIFICATION

LFC-Bonding alloy with a wide spectrum of indications – free of nickel and beryllium –
  • High bonding strength with low fusing ceramic masses (e.g. CARRARA, VITA VM 15, Duceragold Kiss).
  • Highly corrosion resistant.
  • Bio-compatible.
  • Especially patient-friendly due to a low thermal conductivity.
  • Wide spectrum of indications; also for large bridges.
  • Thermal expansion coeffi cient of 15,9.
  • Light oxide.
  • Suitable for laser welding.
Composition:
Co Cr Fe Mo Si Mn Andere Bestandteile <1%
34 % 28,5 % 30 % 5 % 1 % 1 %
 N, C
Technical properties:    


  Other properties:
Proof stress 580 MPa  

Ultimate tensile strength 860 MPa   Density 8.1 g/cm³
Tensile elongation 11 %   Solidus-Liquidus interval 1300 - 1370°C
Elastic modulus 195-205 GPa   Casting temperature 1470 - 1520°C
Vickers hardness 315 HV 10   Thermal expansion coeffi cient 15.9 μm/m °C
  REF
1000 g 134000
250 g 134250

Starbond Ni
Starbond Ni
REF - 131000
NiCr-quality bonding alloy – free of beryllium– ...

█ SPECIFICATION

NiCr-quality bonding alloy – free of beryllium–
  • Bio-compatible and corrosion resistant.
  • Especially patient-friendly due to a low thermal conductivity.
  • Ease of processing and polishing due to a low hardness of 200 HV.
  • No cooling period necessary as long as the ceramics used allows for it.
  • A thermal expansion coeffi cient of 14,0 ensures fl exibility when choosing the ceramics.
  • Light oxide.
  • High bonding strength with ceramic masses.
  • Suitable for laser welding.
Composition:
Ni Cr Mo Fe Si
Other elements <1%
60.7 % 24.0 % 11.0 % 1.5 % 1.8 %
 C
Technical properties:    


  Other properties:
Proof stress 340 - 355 MPa  

Ultimate tensile strength 490 - 510 MPa   Density 8.2 - 8.3 g/cm³
Tensile elongation 5 %   Solidus-Liquidus interval 1380 - 1410°C
Elastic modulus 200 GPa   Casting temperature 1510 - 1560°C
Vickers hardness 200 HV   Thermal expansion coeffi cient 14 μm/m °C
  REF
1000 g 131000

MoguCera N
MoguCera N
REF - Table
NiCr-bonding alloy – free of beryllium– ...

█ SPECIFICATION

NiCr-bonding alloy – free of beryllium–
  • Bio-compatible and corrosion resistant.
  • Especially patient-friendly due to a low thermal conductivity.
  • Ease of processing and polishing due to a low hardness of 245 HV .
  • A thermal expansion coeffi cient of 14,4 ensures fl exibility when choosing the ceramics.
  • High bonding strength with ceramic masses.
  • Suitable for laser welding.
Composition:
Ni Cr Mo Si Other ingredients <1%
62 % 24 % 11 % 1.6 % n.k.
Technical properties:    


  Other properties:
Proof stress 354 MPa  

Ultimate tensile strength 495 MPa   Density 8.2 g/cm³
Tensile elongation 7 %   Solidus-Liquidus interval 1290 - 1352 °C
Elastic modulus 200 GPa   Casting temperature 1450 - 1500 °C
Vickers hardness 245 HV 10   Thermal expansion coeffi cient 14.4 μm/m °C
  REF
1000 g 139000

Starbond Co
Starbond Co
REF - 132000
CoCr-partial denture alloy and bonding alloy. Especially for demanding combined fi xedremovable restorations – free of nickel and beryllium – ...

█ SPECIFICATION

CoCr-partial denture alloy and bonding alloy.
Especially for demanding combined fi xedremovable restorations – free of nickel and beryllium –
  • Extra hard and stable.
  • Suitable for laser welding.
  • Ideal mechanical properties.
  • Easy to process and polish.
  • Universal alloy for partial dentures and ceramic veneering.
Composition:
Co Cr Mo Si Other ingredients <1%
62 % 30 % 5.5 % 1 % C, Fe
Technical properties:    


  Other properties:
Proof stress 500 - 650 MPa  

Ultimate tensile strength 800 - 850 MPa   Density 8.4 g/cm³
Tensile elongation 4 %   Solidus-Liquidus interval 1200 - 1385 °C
Elastic modulus 200 - 230 GPa   Casting temperature 1485 - 1540 °C
Vickers hardness 385 HV   Thermal expansion coeffi cient 14.5 μm/m °C
  REF
1000 g 132000

Modelstar S
Modelstar S
REF - 132100
CoCr-partial denture alloy for the whole spectrum of removable partial dentures – from combined fi xed-removable restorations to clasp-retained dentures – free of nickel and beryllium – ...

█ SPECIFICATION

CoCr-partial denture alloy for the whole spectrum of removable partial dentures – from combined fi xed-removable restorations to clasp-retained dentures – free of nickel and beryllium –
  • Spring hard.
  • Suitable for laser welding.
  • Ideal mechanical properties.
  • Easy to process and polish.
Composition:
Co Cr Mo Other ingredients <1%
62.7 % 29 % 6 % C, Fe, Si
Technical properties:    


  Other properties:
Proof stress 510 - 600 MPa  

Ultimate tensile strength 770 - 780 MPa   Density 8.4 g/cm³
Tensile elongation > 3 %   Solidus-Liquidus interval 1170 - 1390 °C
Elastic modulus 200 - 230 GPa   Casting temperature 1490 - 1540 °C
Vickers hardness 355 HV
  Thermal expansion coeffi cient 15 - 16 μm/m °C
  REF
1000 g 132100
Universal Bonding
Universal Bonding
REF - 271060
Ensures correct bonding of palladium alloys, non-precious metal alloys, economic alloys and ceramics; ...

█ SPECIFICATION

Ensures correct bonding of palladium alloys, non-precious metal alloys, economic alloys and ceramics; ideal substrate for base compounds; prevents discolouring; unproblematic fi ring of bonding golds; suffi cient for around 200 to 300 units.
  REF
Syringe 2 ml with brush 271060

Starbond Lot
Starbond Lot
REF - Table
Soldering sticks for all Starbond alloys – free of nickel and beryllium – ...

█ SPECIFICATION

Soldering sticks for all Starbond alloys – free of nickel and beryllium –
for tension free connections; working temperature: 1200 – 1240° C; fl ux: Pasta Flux
Composition:
Co Cr Mo Si Other ingredients <1%
61.5 % 30 % 4 % 3.5 % B, C, Mn
  REF
25 g 121525
5 g 121526

Starsolder
Starsolder
REF - Table
Ready-to-use universal soldering sticks for all non-precious metal alloys – free of beryllium ...

█ SPECIFICATION

Ready-to-use universal soldering sticks for all non-precious metal alloys – free of beryllium.
Provides well annealed, tension-free connections; working temperature: 1100 – 1150 °C.
Composition:
Co Cr Ni Si Other ingredients <1%
50 % 18 % 17 % 1.8 % k. A.
  REF
25 g 121515
5 g 121516

Starwire
REF - Table
CoCr-Laser welding wire – free of beryllium and nickel ...

█ SPECIFICATION

CoCr-Laser welding wire – free of beryllium and nickel.
Free of carbon; length: 4.3 m
Composition:
Co Cr Mo Other ingredients <1%
65 % 28 % 5.5 % k. A.
  REF
Ø 0.5 mm/4.3 m 121500
Ø 0.35 mm/4.3 m 121600

Pasta Flux
Pasta Flux
REF - 220210
Pasta Flux (the original) is a special soldering paste for precious metal alloys as well as non-precious metal alloys ...

█ SPECIFICATION

Pasta Flux (the original) is a special soldering paste for precious metal alloys as well as non-precious metal alloys (primarily of chromium, cobalt, molybdenum); when used for bonding alloys, capable also of being used after fi ring; no porcelain discolouring.
  • Good flow properties.
  • Universally applicable.
  REF
30 g 220210